Pengaruh Hasil Pengelasan Listrik dan Asetilin pada Plat Bordes terhadap Kekuatan Tarik, Struktur Mikro, Makro dan NDT (Non Destrutive Testing)
DOI:
https://doi.org/10.58192/unitech.v5i`1.4159Keywords:
Acetylene Welding, Electric Welding, Micro-Macro Structure, NDT, Tensile StrengthAbstract
Welding is a metal joining method widely applied in various industrial fields. The quality of welded joints is strongly influenced by the welding method used. This study aims to compare the effect of electric welding and acetylene welding on tread plate in terms of tensile strength, micro-macro structure, and Non-Destructive Testing (NDT) results. The research employed an experimental approach in the laboratory. Tensile testing was conducted to determine yield point and Yield Stress, while macro and microstructural observations were carried out to analyze metallurgical changes. NDT was performed using Magnetic Particle Testing (MPT) and Liquid Penetrant Testing (LPT) to detect possible defects. The results indicate that electric welding produced better joint quality compared to acetylene welding. Specimens welded with electricity showed yield points ranging from 10,045–15,476 N and Yield Stress between 197.663–304.527 MPa, with fewer defects observed. In contrast, acetylene welding produced more varied results with significant defects such as cracks and large porosity, which reduced joint quality. This research demonstrates that electric welding provides superior tensile strength and joint reliability compared to acetylene welding.
References
Agustianti, R., Nussifera, L., Angelianawati, L., Meliana, I., Sidik, E. A., Nurlaila, Q., Simarmata, N., Himawan, I. S., Pawan, E., Ikhram, F., & others. (2022). Metode penelitian kuantitatif dan kualitatif. Tohar Media.
Al Muqtadir, A., Hadjon, Y. R. G., & Samkakai, F. (2022). Alat Uji Tarik Serat Tunggal Digital. Politeknik Negeri Ujung Pandang.
Alwahidi, M. N., Afrizal, B., & others. (2025). Review Pengujian Pengelasan Metode Non-Destructive Test. Jurnal Mema (Jurnal Mesin dan Manufaktur), 2(1), 30-42.
Anis, I. M., Met, M., & Winarto, I. (2025). LAS MATERIAL: Proses penyambungan dan permasalahan yang ditimbulkan. PT. Rayyana Komunikasindo.
AZHARI, M. H. (2023). Pengaruh Kuat Arus Las Listrik SMAW Terhadap Cacat Permukaan Dengan Teknik Uji Penetrant Test Pada Baja ASTM A36. Fakultas Teknik, Universitas Islam Sumatera Utara.
BARUS, R. A. (2025). Analisis Pengaruh Variasi Arus Listrik Pada Sambungan Las SMAW Terhadap Kekuatan Tarik Dan Struktur Mikro Daerah HAZ Pada Baja Karbon Sedang. Fakultas Teknik, Universitas Islam Sumatera Utara.
Fauzi, A. (2021). Uji tarik kekuatan sambungan pengelasan las gesek baja ST 41. DIII Teknik mesin Politeknik Harapan Bersama.
Hadiyastama, M. F., Nurwahidin, M., & Yulianti, D. (2022). Peran teknologi pendidikan dalam pembelajaran abad 21. Jurnal Pengembangan Profesi Pendidik Indonesia, 2(1), 11-18.
Haifan, M., Makosim, S., & Utomo, D. (2024). Analisis Non Destructive Test (NDT) Pada Pengelasan Sambungan Instalasi Pipa Dengan Metode Radiography: Studi Kasus Di Proyek Refinery Development Master Plan (RDMP) Balikpapan.
Nampira, A. A., Sepriano, S., & Judijanto, L. (2025). Teknik Mesin: Teori dan Implementasinya. PT. Green Pustaka Indonesia.
Nur Alamsyah, B., & Suastianti, D. (2025). Analisis Kerusakan Produk Pengelasan Shielded Metal Arc Welding (SMAW) Berbasis Material Plat Baja Astm A36 Untuk Aplikasi Body Kapal. Institut Teknologi Indonesia.
Pakpahan, A. F., Prasetio, A., Negara, E. S., Gurning, K., Situmorang, R. F. R., Tasnim, T., Sipayung, P. D., Sesilia, A. P., Rahayu, P. P., Purba, B., & others. (2021). Metodologi penelitian ilmiah. Yayasan Kita Menulis.
Pratama, H. S. Y., Prianto, K., & Purwatama, A. (2025). Studi Komparasi Konstruksi Baja Dengan Konstruksi Beton Bertulang Ditinjau Dari Segi Struktur Dan Biaya. SISTEM Jurnal Ilmu Ilmu Teknik, 21(1), 35-43. https://doi.org/10.37303/sistem.v21i1.308
Putra, R. D., & Buqi, M. A. (2023). Analisa Pengaruh Heat Treatment dan Variasi Kecepatan Putaran Pada Pengelasan Gesek Baja AISI 1045 Terhadap Kekuatan Tarik Struktur Mikro dan Kekerasan. Institut Teknologi Nasional Malang.
Ramadan, R., & others. (2023). Analisa Kekuatan Impak Dan Struktur Mikro Pengelasan Logam Berbeda ASTM A36 dan AISI 316L Setelah PWHT. Universitas Hasanuddin.
Salim, A. T. A., Aminudin, A., Yuwono, I., Wicaksono, D. A., Siregar, I., Pradana, K. B., Puspita, D. W., Setiani, R. D., Prasetya, R. G. E., Fadilla, F. I., & others. (2023). Terapan Iptek Kewirausahaan Hasil Produk Pengelasan SMAW Untuk Meningkatkan Keterampilan Santri Pondok Pesantren Miftahul Huda Doho, Dolopo. DIKEMAS (Jurnal Pengabdian Kepada Masyarakat), 7(2).
Senopati Rabbani, D. (2025). Analisis Laju Korosi Dan Sifat Mekanik Pada Material Baja ASTM A36 Untuk Rotor Bezier-Savonius Dengan Media Air Laut. Fakultas Teknik Universitas Sultan Ageng Tirtayasa.
Sulistiyo, B., Purwanto, H., & Syafa'at, I. (2021). Analisis Pengaruh Arus Pengelasan GMAW Terhadap Struktur Makro, Mikro dan Sifat Mekanik Pada Material Baja Karbon ASTM A36. Momentum, 17(1), 36-42. https://doi.org/10.36499/mim.v17i1.4346
SYAHRIN, A. (2025). Studi Eksperimental Perbandingan Ketangguhan Antara Las Listrik Dengan Las Asitelin Terhadap Baja SS400. Fakultas Teknik, Universitas Islam Sumatera Utara.
Utomo, W. B., & Hasan, B. (2022). Penentuan Laju Korosi Baja Konstruksi Menggunakan Metode Tafel Analisis. Seminar Nasional Hasil Penelitian & Pengabdian Kepada Masyarakat (SNP2M), 7, 19-24.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Jurnal Universal Technic
This work is licensed under a Creative Commons Attribution 4.0 International License.