Analisis Kualitas Sambungan Las Kampuh V dan Double V Menggunakan Self Shielded Fcaw pada Baja Karbon Rendah Astm A36 Uji Dpt, Tarik dan Bending
DOI:
https://doi.org/10.58192/unitech.v4i2.4102Keywords:
ASTM A36, Double V-Groove, FCAW-SS, Quality Of Welded Joint, V-GrooveAbstract
This research was conducted to evaluate the weld joint quality of V-groove and double V-groove configurations on ASTM A36 low carbon steel using the Self Shielded Flux-Cored Arc Welding (FCAW-SS) method. ASTM A36 was selected as the base material due to its favorable mechanical properties, excellent weldability, and wide application in construction and manufacturing. The welding process was carried out on steel plates with a thickness of 10 mm using E71T-1C wire, under controlled parameters of 140 A current, 24 V voltage, and 1G welding position. The weld quality was assessed through Dye Penetrant Testing (DPT), tensile testing, and bending testing. The Dye Penetrant Testing DPT results showed that the double V-groove joints exhibited fewer and smaller surface defects compared to the V-groove joints, indicating better weld homogeneity. Tensile testing demonstrated an average maximum strength of 277.645 MPa for the V-groove and 301.904 MPa for the double V-groove, reflecting an improvement of approximately 8.7% in the double V-groove. The bending tests revealed that the double V-groove joints were able to maintain structural integrity without significant cracks, while the V-groove joints tended to show defect indications under bending loads. Based on these findings, the double V-groove configuration is considered superior in terms of both strength and toughness, and therefore recommended for structural and manufacturing applications requiring high-quality joints in ASTM A36 low carbon steel.
References
Albrecht, P., & Huber, M. (2017). Welding distortion in V-groove welds: A review. Welding Journal.
American Society of Mechanical Engineers. (n.d.). ASME Section IX: Welding, brazing, and fusing qualifications.
American Welding Society. (2020). AWS D1.1/D1.1M:2020: Structural welding code—Steel.
ASTM International. (2014). ASTM A36/A36M-14: Standard specification for carbon structural steel plates.
ASTM International. (2014). ASTM E190/E290-14: Standard test methods for bend testing of metallic materials.
ASTM International. (2018). ASTM E165/E165M-18: Standard practice for liquid penetrant testing.
ASTM International. (2021). ASTM E8/E8M-21: Standard test methods for tension testing of metallic materials.
Brown, S., & Miller, T. (2013). Welding technology fundamentals. McGraw-Hill.
Callister, W. D., & Rethwisch, D. G. (2018). Materials science and engineering: An introduction (10th ed.). Wiley.
Chen, H., & Wang, Y. (2015). The effect of joint design on the mechanical properties of welded joints. Journal of Constructional Steel Research.
Davis, J. (2001). Alloying elements in stainless steel and other speciality steels. ASM International.
García, R., López, J., & Martínez, A. (2019). Evaluation of V-groove welds in structural applications. Journal of Materials Engineering and Performance.
Gunawan, R., & Santoso, A. (2020). Analisis kekuatan tarik sambungan las kampuh double V pada pelat baja karbon sedang. Jurnal Rekayasa Manufaktur, 5(2), 112–120.
Huang, Y., Zhang, L., & Wang, J. (2019). Weld joint design and its impact on structural integrity. International Journal of Structural Engineering.
Kumar, R., & Singh, A. (2018). Comparative study of V-groove welds. International Journal of Engineering Research and Applications.
Kwon, Y., & Lee, J. (2014). The influence of welding parameters on the quality of V-groove welds. Welding Journal.
Liu, J., & Zhang, Y. (2018). Fatigue behavior of V-groove welds. Materials Science and Engineering: A.
Mendez, J., & Torres, R. (2021). Optimization of welding parameters for V-groove welds. Journal of Materials Processing Technology.
Miller, J. (2011). Welding principles and applications. Cengage Learning.
Patel, R., & Kumar, S. (2020). Mechanical properties of welded joints: A review. Materials Science and Engineering: A.
Prasetyo, D., & Lestari, S. (2021). Studi komparatif distorsi pada pengelasan kampuh single V dan double V menggunakan metode FCAW. Prosiding Seminar Nasional Rekayasa Proses, 134–142.
Purwanto, P., Wa’adduulloh, M., & Widdo, R. (2024). Analisis pengaruh variasi hasil pengelasan FCAW antara material Grade A terhadap macro structure test di insert plate ship deck ramah lingkungan. Jurnal Saintek Maritim, 24(2), 225–234.
Ramadhan, F., & Aditama, G. (2020). Pengaruh desain kampuh double V terhadap sifat mekanik hasil las SMAW pada baja SS400. Jurnal Aplikasi Teknik Mesin, 4(1), 25–32.
Setiawan, H., & Abdullah, M. (2020). Optimalisasi desain kampuh las double V untuk aplikasi struktur kapal. Jurnal Teknologi Kelautan, 8(1), 45–56.
Setyawan, R., & Wijaya, B. (2022). Pentingnya preparasi kampuh las dalam menjamin kualitas sambungan material logam. Buletin Teknik Las Indonesia, 2(1), 1–8.
Smith, R., & Jones, T. (2020). Versatility of V-groove welds in industrial applications. Journal of Engineering Materials and Technology.
Supriyanto, A., & Utami, D. (2021). Pengaruh celah akar terhadap penetrasi las pada sambungan kampuh double V. Jurnal Ilmiah Teknik Industri, 9(3), 190–197.
Suryadi, T., & Wijaya, P. (2019). Evaluasi radiografi cacat las pada sambungan kampuh double V menggunakan metode GTAW. Majalah Teknik Mesin, 12(2), 78–85.
Utomo, C., & Susilo, E. (2021). Tinjauan umum proses pengelasan dan aplikasinya di industri manufaktur. Jurnal Teknik Material, 6(1), 1–10.
Wibowo, A., Nugroho, D., & Lestari, P. (2023). Karakteristik geometri kampuh double V pada pengelasan baja tebal. Jurnal Material dan Proses, 7(1), 30–38.
Yusuf, A., & Hasanah, N. (2023). Pengaruh sudut bevel terhadap kekuatan tarik sambungan las baja karbon. Jurnal Rekayasa Material dan Metalurgi, 1(1), 1–9.
Zhang, X., Li, Y., & Chen, Z. (2021). Enhancement of mechanical properties of V-groove welds through alloying. Materials Science and Engineering: A.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Jurnal Universal Technic
This work is licensed under a Creative Commons Attribution 4.0 International License.