Analisa Pengaruh Variasi Bevel Dan Penggunaan Backing Ceramic Terhadap Kekuatan dan Defect Material Baja Grade A Pengelasan Shield Metal Arc Welding (SMAW)
DOI:
https://doi.org/10.58192/unitech.v4i1.3701Keywords:
Bevel Variation, Ceramic Backing, Mechanical Strength, Grade A Steel, Shield Metal Arc Welding (SMAW)Abstract
Grade A steel plates are commonly used in marine and offshore structures due to their high corrosion resistance. This study investigates the effect of bevel angle variations (30°, 40°, and 50°) and the use of ceramic backing on the mechanical properties and welding defects of Grade A steel using the Shielded Metal Arc Welding (SMAW) method. Welding was conducted with four-pass multipass welding. An experimental approach was employed, including macro visual inspection, dye penetrant, tensile, and impact testing. Results showed that specimens without ceramic backing (P1) had more defects such as incomplete penetration and spatter compared to those with backing (P2). All specimens met ASTM E23 impact standards (average 23.9–24.1 J/mm²). Tensile tests revealed that ceramic backing improved strength, with the highest UTS (576.1 MPa) and elongation (25%) found.
References
Annual Hand Book ASTM E23 – 02. Standard Test Methods for Notched Bar Impact Testing of Metallic Materials 1. (Mar 02, 2021)
A. INTERNATIONAL, ASTM E8/E8M16a, Standard Test Methods for Tension Testing of Metallic Materials, Volume 03.01. 2016.
Allpro.com (2021) Jenis Jenis Cacat Pengelasan. Diakses pada 12 Juni 2025 Pukul 23.15 WIB. Dari https://www.allpro.co.id/cacat-las/
Benami I.G. Sembiring, Untung Budiarto, & Parlindungan Manik. (2024). Analisis Pengaruh Variasi Kuat Arus Listrik dan Posisi Pengelasan Shielded Metal Arc Welding (SMAW) Terhadap Kekuatan Material Baja Karbon Sedang. Jurnal Teknik Perkapalan, 12. https://ejournal3.undip.ac.id/index.php/naval
Candra Wahyu Setyawan, Syaripuddin, Ahmad Lubi, & Ferry Budhi Susetyo. (2022). Jurnal Asiimetrik: Jurnal Ilmiah Rekayasa Dan Inovasi Pengaruh Suhu Pengeringan Elektroda E 7018 Terhadap Hasil Pengelasan Material A36 Drying Temperature Effect of E 7018 Electrode on Weld Joint of A36 Material. 4, 209–220.
Ikhsanudin Ramadhan, Rilo Chandra Muhamadin, & Ilham Arifin Pahlawan. (2024). Analisis Kegagalan Pada Hasil Pengelasan Di PT. Autokorindo Pratama. Jurnal Enigma: Engineering In Green Machinery (Vol. 1, Issue 1).
Indah Purmayanti, & Kurniawati Oktarina. (2020). Aplikasi Welding Procedure Specification (Wps) Dengan Bevel 300 Untuk Pengelasan Konstruksi Kapal Tanker 3500 Ltdw Hn. 309 Pada Uji Bending Di Pt. Daya Radar Utama Unit Iii Lampung (Vol. 5, Issue 1).
Juswan Sade. (2023). Improve Competence to Complete the Requirements for International Welder Part of the Book Series “Material and Structure Engineering” Calculation of Elongation in Media Use Backing Ceramic against Steel ASTM A36 by SMAW Process.
Kawatlas.jayamanunggal.com. (2025) Tentang Mesin Las SMAW. Diakses Pada Tanggal 25 Mei 2025, Pukul 22.13 WIB. Dari https://kawatlas.jayamanunggal.com/tentang-mesin-las-smaw/
Megaperkakas.com. (2020). Jenis-Jenis Sambungan Pengelasan. Diakses Pada Tanggal 12 juli 2025, Pukul 23.30 WIB. Dari https://megaperkakas.com/5-jenis-sambungan-las/
Muhammad Abdul Aziz Mufti, A., Budiarto, U., & Hadi, S. (2021). Jurnal Teknik Perkapalan Analisis Pengaruh Variasi Sudut Kampuh Single V dan Variasi Posisi Las dengan Sambungan MIG pada Aluminium 6061 terhadap Kekuatan Impak sebagai Material Kapal. Jurnal Teknik Perkapalan, 9(1), 23. https://ejournal3.undip.ac.id/index.php/naval
Muhammad Alfi Rachmawan, & Erifive Pranatal. (2023). Analisis Kekuatan Hasil Las Backing Ceramic Pada Proses Pengelasan Fcaw Material Baja Karbon A36. Ocean Engineering : Jurnal Ilmu Teknik Dan Teknologi Maritim, 2(2), 97–110. https://doi.org/10.58192/ocean.v2i2.1150
Mu’izzaddin Wa’addulloh, Purwanto Purwanto, Virgiawan Toti. (2023). Analisis Pengaruh Arus Dan Tegangan Pngelasan Smaw Terhadap Struktur Dan Sifat Baja Carbon Grade A Dan Grade B. Jurnal Sains dan Teknologi Vol. 2 No. 2 Desember 2023. OI: https://doi.org/10.58169/saintek.v2i2.221
Mu’izzaddin Wa’addulloh, Anisa Diansisti, & Purwanto. (2023). Analisis Pengaruh Arus dan Tegangan Pengelasan 3 G Conveyor Terhadap Struktur dan Sifat Baja. Ocean Engineering : Jurnal Ilmu Teknik Dan Teknologi Maritim, 2(3), 83–93. https://doi.org/10.58192/ocean.v2i3.1965
Njswelding.com. (2025) Konstruksi Mesin Las SMAW. Diakses pada tanggal 13 juli 2025 Pukul 00.13 WIB. Dari https://www.ncjswelding.com/products/a-type-welding-ceramic-backing-with-adhesive-tape-ceramic-weld-backing-strip.
Purwanto, Mu’izzaddin Wa’adduulloh, & Risriki Widdo. (2024). Analisis Pengaruh Variasi Hasil Pengelasan Fcaw Antara Material Grade A. Jurnal Saintek Maritim. Vol. 24 No. 2
Renita Wurdhani, Untung Budiarto, & Wilma Amiruddin. (2021). Pengaruh Perlakuan Panas (Heat Treatment) Normalizing Terhadap Kekuatan Impak Aluminium 6061 Pengelasan MIG dengan Variasi Posisi dan Bentuk Kampuh. Jurnal Teknik Perkapalan, Vol. 9. https://ejournal3.undip.ac.id/index.php/naval
Rifa’I Abubakar, 2021, Pengantar Metodologi Penelitian, Yogyakarta : SUKA-Press UIN Sunan Kalijaga.
Rita Kumala Sari et al, 2023, Metodologi Penelitian Pendidikan, Banten : PT. Sada Kurnia Pustaka.
Sarjito Joko Sisworo, M. (2010). Pengaruh Perbedaan Posisi Pengelasan Terhadap Kekuatan Sambungan. 7 . (Jurnal Ilmu Pengetahuan dan Teknologi Kelautan).Vol 7.
Setyo Firman Alamsyah. (2022). Studi Kekuatan Tarik, Kekerasan, Dan Struktur Makro Pada Hasil Pengelasan Smaw Material Baja Karbon Rendah Menggunakan E6013 Dengan Penambahan Krom. Jurnal Pendidikan Teknik Dan Vokasional, 5(1), 20–26. https://doi.org/10.21009/jptv.5.1.20
Sulibersama.com (2024) Jenis-Jenis Cacat Pengelasan. Diakses pada 12 juli 2025. Pukul 23.25 WIB. Dari https://sulybersama.com/tag/defect-in-welding/
Syaripuddin, Setyo Firman Alamsyah, & Ferry Budhi Susetyo. (2021). Pengaruh Krom pada Sambungan Las Terhadap Sifat Mekanik Baja Karbon dengan Elektroda E 6013. Jurnal Asiimetrik: Jurnal Ilmiah Rekayasa Dan Inovasi, 3(Pengaruh Krom pada Sambungan Las Terhadap Sifat Mekanik Baja Karbon dengan Elektroda E 6013), 9–16.
Yhudo Nuhgraha, M.Khairul Amri Rosa, & Indra Agustian. (2020). Perancangan Alat Uji Impak Digital dengan Metode Charpy Untuk Mengukur Kekuatan Material Polimer. Jurnal Amplifier, 10 no 2(Perancangan Alat Uji Impak Digital dengan Metode Charpy Untuk Mengukur Kekuatan Material Polimer).
Yusuf Rizal Fauzi, Anhar Khalid, & Akmal Barry. (2022). Pengaruh variasi bevel pada proses pengelasan SMAW terhadap kekuatan tarik material. ARMATUR : Artikel Teknik Mesin & Manufaktur, 3(2), 58–63. https://doi.org/10.24127/armatur.v3i2.2694
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2025 Jurnal Universal Technic
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.